Combined Modification of Dual-Phase Li₄Ti₅O₁₂-TiO₂ by Lithium Zirconates to Optimize Rate Capabilities and...

The low electrical conductivity and ordinary lithium-ion transfer capability of Li₄Ti₅O₁₂ restrict its application to some degree. In this work, dual-phase Li₄Ti₅O₁₂-TiO₂ (LTOT) was modified by composite zirconates of Li₂ZrO₃, Li₆Zr₂O₇ (LZO) to boost the rate capabilities and cyclability. When the homogeneous mixture of LiNO₃, Zr(NO₃)₄·5H₂O and LTOT was roasted at 700 °C for 5 h, the obtained composite achieved a superior reversible capacity of 183.2 mAh g^-1 to the pure Li₄Ti₅O₁₂ after cycling at 100 mA g^-1 for 100 times due to the existence of a scrap of TiO₂. Meanwhile, when the composite was cycled by consecutively doubling the current density between 100 and 1600 mA g^-1, the corresponding reversible capacities are 183.2, 179.1, 176.5, 173.3, and 169.3 mAh g^-1, signifying the prominent rate capabilities. Even undergoing 1400 charge/discharge cycles at 500 mA g^-1, a reversible capacity of 144.7 mAh g^-1 was still attained, denoting splendid cyclability. From a series of comparative experiments and systematic characterizations, the formation of LZO meliorated both the Li⁺ migration kinetics and electrical conductivity on account of the concomitant superficial Zr⁴⁺ doping, responsible for the comprehensive elevation of the electrochemical performance.