Hydrophilic Stent Coating Inhibits Platelet Adhesion on Stent Surfaces: Initial Results In Vitro

Endovascular stents and flow diverter stents (FDS) have revolutionized the treatment of intradural aneurysms; however, the need for dual anti-platelet treatment (DAPT) limits their use and can cause additional issues. Therefore, there is a need to develop stent coatings that negate the need for DAPT.

Two different hydrophilic polymer coatings (HPC-I and HPC-II) were used to coat small nickel titanium plates to initially test the hydrophilic properties of these coatings when applied to nickel titanium. The plates were subsequently incubated with non-medicated whole blood from healthy volunteers for 10 min and stained with a CD61 immunofluorescent antibody that allows detection of adherent platelets. The coatings were applied to FDS wires and were again incubated with non-medicated whole blood from the same volunteers. Scanning electron microscopy was used to detect adherent platelets on the wire surface.

The HPC-II coating (1.12 ± 0.4%) showed a significantly lower CD61 +ve cell count (p ≤ 0.001) compared to both uncoated NiTi plates (48.61 ± 7.3%) and those with the HPC-I coating (mean 40.19 ± 8.9%). Minimal adherent platelets were seen on the FDS nickel titanium wires coated with the HPC-II compared to uncoated FDS under electron microscopy.

There is a significant decrease in the number of adherent CD61 +ve platelets on nickel titanium surfaces coated with the HPC-II coating compared to uncoated surfaces. The coating can be successfully applied to the wires of flow diverters. The results of this study are promising with regard to the development of new anti-thrombogenic endovascular devices.