The push-out bond strength of calcium silicate-based endodontic sealers
David Donnermeyer1, Pia Dornseifer2, Edgar Schäfer3
1Department of Periodontology and Operative Dentistry, Westphalian Wilhelms-University, Albert-Schweitzer-Campus 1, building W 30, 48149, Münster, Germany. David.Donnermeyer@ukmuenster.de.
Background:
The aim was to compare the dislodgement resistance of calcium silicate-based sealers (Total Fill BC Sealer, Endo CPM Sealer, BioRoot RCS) with an epoxy resin-based sealer (AH Plus).
Methods:
The root canals of 80 single-rooted human teeth were instrumented with F360 up to size 45.04. All canals were obturated using matching gutta-percha cones according to the single-cone technique in combination with one of the mentioned sealers (n = 20 per group). After eight weeks of incubation (37 °C, 100% humidity), the roots were embedded in resin. Starting with a distance of 7 mm from the apex, four slices of 1 mm thickness were cut. Dislodgement resistance was measured using a universal testing machine and the push-out bond strength was calculated. Specimens were examined under 4×-magnification to determine the mode of bond failure. Statistical analysis was performed using ANOVA and Student-Newman-Keuls-test.
Results:
Regarding the pooled data of all sections, the push-out bond strength of AH Plus was significantly higher than the push-out bond strength of all calcium silicate-containing sealers (P < 0.05). Out of all calcium silicate-based sealers, Total Fill BC Sealer showed the highest push-out bond strength (P < 0.05). BioRoot RCS had significant higher push-out bond strength than Endo CPM Sealer (P < 0.05). Nearly the same results were found for all four sections. BioRoot RCS only differed significantly from Endo CPM Sealer in the third section (P < 0.05).
Conclusions:
The push-out bond strength of the investigated calcium silicate-based sealers was lower than of AH Plus. Total Fill BC showed the highest push-out bond strength of the calcium silicate-based sealers.
More Related Videos
Related Concept Videos
01:12Bonding and Strength of Aggregate
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
02:29Relative Strengths of Conjugate Acid-Base Pairs
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:35Acid and Bases: Ka, pKa, and Relative Strengths