Physical and mechanical properties of dual functional cements-an in vitro study
Juliana Ghelen Walcher1, Vicente Castelo Branco Leitune2, Fabricio Mezzomo Collares1
1Dental Materials Laboratory, School of Dentistry, Universidade Federal do Rio Grande do Sul, Ramiro Barcelos 2492, Porto Alegre, Rio Grande do Sul, Brazil.
Objectives:
The aim of this study was to evaluate the physical and mechanical properties of different dual functional cements.
Materials And Methods:
Three dual functional cements (Allcem Core (FGM), Rebilda DC (VOCO), and LuxaCore Z (DMG)), a luting resin cement (Rely X ARC (3 M ESPE)), and a Core Buildup composite resin GrandioSo (VOCO) were used. Flexural strength (n = 10) and film thickness (n = 6) were evaluated according to ISO 4049:2009. Flow (n = 6) was evaluated according to ISO 6876:2001. Degree of conversion (DC) was assessed immediately and 24 h after polymerization (n = 5). For resistance to dislodgment (RD) analysis, bovine teeth were prepared to receive fiber glass posts, and a push-out test (n = 12) was used.
Results:
Luxacore Z presented lower flexural strength when compared to GrandioSo (p < 0.001). No statistical difference was found between cements for film thickness (p = 0.66). Reduced flow values were found for Allcem Core (p = 0.006). No statistical difference was found for immediate DC for different cements (p > 0.05). After 24 h, DC increased for all groups, except for Luxacore Z (p = 0.054). The RD did not differ from the control Rely X ARC, regardless of the root third (p > 0.05). Luxacore Z showed lower mean values in the apical third compared to the coronal third (p = 0.046).
Conclusions:
The dual functional cements (Allcem Core and Rebilda DC) possessed similar physical and mechanical properties of luting resin cement (RelyX ARC) and Core Buildup composite resin (GrandioSo). Hence, they could be used for one-stage post and core buildup restorations.
Clinical Relevance:
The dual functional cements could be used for one-stage post and core buildup restorations since they possess similar physical and mechanical properties of luting resin cements and Core Buildup composite resin.
Related Concept Videos
02:57Physical and Chemical Properties of Matter
01:26Physical Properties of Amines
02:19Physical Properties Affecting Solubility
As for any solution, the solubility of a gas in a liquid is affected by the attractive intermolecular forces between solute and solvent species. Unlike solid and liquid solutes, however, there is no solute-solute intermolecular attraction to overcome when a gaseous solute dissolves in a liquid solvent since the atoms or molecules comprising a gas are far separated and experience negligible interactions. Consequently, solute-solvent interactions are the sole...
02:33Physical Properties of Alkanes
02:17Physical Properties of Ethers
An ether molecule has a net dipole moment due to the polarity of C–O bonds. Subsequently, boiling points of ethers are lower than those of alcohols of comparable molecular weight and slightly higher than those of hydrocarbons of comparable molecular weight (Table 1).
Ethers can act as hydrogen bond acceptors, making them more water-soluble than hydrocarbons, but since ethers cannot act as hydrogen bond donors, they are much less soluble in water than alcohols. Ethers are considered...
01:18Urine: Physical and Chemical Properties
The concentration of these solutes varies, with urea being the most abundant nitrogenous waste product. Other solutes include sodium, chloride, potassium, phosphate,...