Low intensity sonosynthesis of iron carbide@iron oxide core-shell nanoparticles

Here we demonstrate a simple method for the organic sonosynthesis of stable Iron Carbide@Iron Oxide core-shell nanoparticles (ICIONPs) stabilized by oleic acid surface modification. This robust synthesis route is based on the sonochemistry reaction of organometallic precursor like Fe(CO)₅ in octanol using low intensity ultrasonic bath. As obtained, nanoparticles diameter sizes were measured around 6.38 nm ± 1.34 with a hydrodynamic diameter around 25 nm and an estimated polydispersity of 0.27. Core-Shell structure of nanoparticles was confirmed using HR-TEM and XPS characterization tools in which a core made up of iron carbide (Fe₃C) and a shell of magnetite (γ-Fe₂O₃) was found. The overall nanoparticle presented ferromagnetic behavior at 4 K by SQUID. With these characteristics, the ICIONPs can be potentially used in various applications such as theranostic agent due to their properties obtained from the iron oxides and iron carbide phases.