Microcrack Analysis of Dental Hard Tissue After Root Canal Irradiation with a 970-nm Diode Laser

The aim of the present study was to investigate differences in the amount of dentin microcracking caused by the use of a 970-nm diode laser with different parameters for endodontic disinfection procedures.

Forty dental roots underwent mechanical endodontic preparation in a standardized manner. Each sample was randomly allocated to 4 groups receiving constant or interval laser irradiation time, calcium hydroxide disinfection, or a control group, with 10 samples per group. Transmission microscopy of all samples was performed at T0, before preparation; T1, immediately after endodontic preparation; and T2, after laser application in the laser groups and after 1 week of storage in the control and calcium hydroxide groups. The microcracks at each measurement point were color labeled, layered, and compared.

No significant differences were noted at T0 and T1 (p > 0.05). Statistically significant differences in the overall amount of microcracking were observed between the constant laser group and all other groups at T2 (p < 0.05). There were no statistically significant differences between the interval laser group, the calcium hydroxide group, and the control group at T2 in relation to the overall amount of microcracking (p > 0.05). When the root sections were analyzed separately, the coronal section did not show any statistically significant differences between the constant laser and interval laser groups (p > 0.05). The middle and apical root sections in the constant laser group showed the significantly largest amount of crack formation in comparison with the other groups (p < 0.05). The statistically significantly smallest amount of crack formation was observed in the apical third for all groups (p < 0.05).

Clinically proposed laser protocol seems to be able to prevent side effects to the tissue, such as microcracks of the root canal dentine.