Investigation of multifilament MgB₂ superconducting joint technique for development of MRI magnets

This study presents the investigation of superconducting joints fabricated using multifilament magnesium diboride (MgB₂) wires for the development of persistent-current mode magnetic resonance imaging (MRI) magnets. The critical current of the jointed samples decreased with increasing cutting angle because the smaller cutting angle allowed greater exposure of the MgB₂ filament, thereby increasing the contact area for the wire-bulk-wire connection. In addition, an appropriate pressing pressure (300 MPa) was necessary to establish the multifilament MgB₂ joint without significant degradation of superconducting properties. The resistance of the optimal MgB₂ joint, measured using the field-decay technique, was <1.5 × 10^-14 Ω. Therefore, the proposed joint technique can be employed for developing multifilament MgB₂ MRI magnets operating in the persistent-current mode.