Effect of reducing acid-etching duration time on compressive strength and bonding of a universal adhesive to calcium
F Shafiei1, M Doozandeh2, F Gharibpour2
1Oral and Dental Disease Research Center, Department of Operative Dentistry, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.
Aim:
To assess the effect of acid-etching duration time on the compressive strength, microstructure and shear bond strength of All-Bond Universal adhesive to MTA-Angelus (AMTA), and Biodentine (BD).
Methodology:
Forty-eight cylindrical specimens (4 mm in diameter, 6 mm in height) of AMTA in four groups and 48 specimens of BD in four groups (n = 12) were prepared and stored for 72 h. The control groups were unetched whilst the three experimental groups were acid-etched for 5, 10 and 15 s, respectively, followed by compressive strength testing. The effect of the various acid-etching times on surface micromorphology was evaluated under a scanning electron microscope. Similar groups were bonded using All-Bond Universal and Aelite Flo and shear bond strength was tested. Data were analysed using two-way ANOVA and Tukey tests.
Results:
10-s and 15-s acid-etching reduced the compressive strength of AMTA and BD (P < 0.001), while 5-s etching did not (P ≤ 0.86). In all the groups, BD had greater compressive strength compared to AMTA. Contrary to BD, the three etched AMTA groups had significantly higher shear bond strength compared to the control group (P < 0.001), with no significant differences between them. The etched groups of AMTA had shear bond strengths comparable to all the BD groups. Scanning electron microscope observations indicated variable surface morphologies such as remnant crystals and cracking/eroding in all our groups of AMTA; though these differences were less prominent for BD.
Conclusions:
Shortening the acid-etching time to 5 s resulted in a beneficial effect in terms of resin bonding for AMTA while preventing the detrimental effect of 10-s and 15-s etching on the compressive strength of AMTA and BD. However, the three etching times had no effect on resin-BD bond.
More Related Videos
06:54Evaluation of the Interplay Between the Complement Protein C1q and Hyaluronic Acid in Promoting Cell Adhesion
Published on: June 15, 2019
06:49Reduced Itraconazole Concentration and Durations Are Successful in Treating Batrachochytrium dendrobatidis Infection in Amphibians
Published on: March 14, 2014
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
01:12Bonding and Strength of Aggregate
01:30Relation Between Tensile Strength and Compressive Strength of Concrete
02:29Relative Strengths of Conjugate Acid-Base Pairs
01:12Setting Time of Cement