A zinc-doped endodontic cement facilitates functional mineralization and stress dissipation at the dentin surface

The purpose of this study was to evaluate nanohardness and viscoelastic behavior of dentin surfaces treated with two canal sealer cements for dentin remineralization.

Dentin surfaces were subjected to: i) 37% phosphoric acid (PA) or ii) 0.5 M ethylenediaminetetraacetic acid (EDTA) conditioning prior to the application of two experimental hydroxyapatite-based cements, containing sodium hydroxide (calcypatite) or zinc oxide (oxipatite), respectively. Samples were stored in simulated body fluid during 24 h or 21 d. The intertubular and peritubular dentin were evaluated using a nanoindenter to assess nanohardness (Hi). The load/displacement responses were used for the nano-dynamic mechanical analysis to estimate complex modulus (E*) and tan delta (δ). The modulus mapping was obtained by imposing a quasistatic force setpoint to which a sinusoidal force was superimposed. AFM imaging and FESEM analysis were performed.

After 21 d of storage, dentin surfaces treated with EDTA+calcypatite, PA+calcypatite and EDTA+oxipatite showed viscoelastic discrepancies between peritubular and intertubular dentin, meaning a risk for cracking and breakdown of the surface. At both 24 h and 21 d, tan δ values at intertubular dentin treated with the four treatments performed similar. At 21 d time point, intertubular dentin treated with PA+oxipatite achieved the highest complex modulus and nanohardness, i.e., highest resistance to deformation and functional mineralization, among groups.

Intertubular and peritubular dentin treated with PA+oxipatite showed similar values of tan δ after 21 d of storage. This produced a favorable dissipation of energy with minimal energy concentration, preserving the structural integrity at the dentin surface.