Water-soluble carboxymethylchitosan used as corrosion inhibitor for carbon steel in saline medium

Biodegradability and ecotoxicity of products used in oil industry are of great relevance and corrosion inhibitor could not be an exception. In earlier reports, chitosan and some derivatives were evaluated as corrosion inhibitors at acid pH, mainly due to polymer solubility. An eco-friendly corrosion inhibitor with water solubility in all pH range should be ideal, as well as that could act under the high salinity of oil field environment. Thus, herein is presented the performance of a water-soluble carboxymethylchitosan (CMC) as corrosion inhibitor in presence of chlorides (3.5% NaCl) in 1020 carbon steel, without any addition of acid or base. CMC showed good properties as corrosion inhibitor in media containing Cl^-, and behaved as an anodic inhibitor. CMC exhibited inhibitory efficiency of about 80% and 67%, according to Tafel curve and electrochemical impedance, respectively, which was attributed to chemisorption mechanism (ΔG_ads ≈ -45 kJ/mol).