Detection of Defects in Reinforced Concrete Structures Using Ultrasonic Nondestructive Evaluation with Piezoceramic...

Reinforced concrete is of vital importance in many civil and industrial structural applications. The effective bonding between steel and concrete is the core guarantee of the safe operation of the structures. Corrosion or other interface debonding in steel-concrete is a typical failure mode during the long service period of the structures, which can severely reduce the load-bearing capacity. The Non-destructive Evaluation technique has been applied to civil engineering structures in recent years. This paper investigates the evaluation of reinforced concrete structures that have interface defects, including the cross-sectional loss and cracks, by using the piezoceramic induced ultrasonic wave and time reversal method. Ultrasonic wave is used as actuating wave to obtain the signals with defect information. Time reversal method is applied to localize and characterize defect along the interface of the steel-concrete and to image the defect through the cross-sectional scanning. Experiments were conducted to perform Nondestructive Evaluation by using six reinforced concrete components with different levels of defects. The invisible damages were made by the cutting part of the steel and embedding a table tennis ball inside concrete structures. The results show that the time reversed method can locate and evaluate the defects along the steel reinforced concrete, and the obtained defect images at the cross-section of the concrete structure are accurate.