Long-term effects of various cleaning methods on polypropylene/ethylene copolymer retainer material

To evaluate long-term light transmittance, surface roughness, and flexural modulus of polypropylene/ethylene copolymer retainer material after exposure to different cleaning methods.

Standardized polypropylene/ethylene copolymer retainer specimens (n = 70, 50.8 mm × 12.7 mm × 1.0 mm) were subjected to seven chemical cleaning solutions: Invisalign cleaning crystals, Retainer Brite, Polident, Listerine mouthwash, 2.5% acetic acid, 0.6% NaClO, and 3% H₂O₂ for 6 months. The specimens were exposed to the different solutions twice a week for 15 minutes or according to manufacturer's instructions, then stored in artificial saliva at 37°C. Another group of specimens (n = 10) were brushed with a standardized toothbrushing machine for 2 minutes twice a week. At baseline and 6 months, light transmittance, surface roughness, and flexural modulus of the specimens were quantified using spectrophotometry, profilometry and three-point bend testing, respectively. Qualitative analysis was performed using a scanning electron microscope (SEM). Statistical analyses were performed at a significance level of .05.

The results showed that light transmittance decreased significantly from baseline for all cleaning methods at 6 months. For an individual method, no significant differences were observed between specimens at baseline and 6 months in surface roughness and flexural modulus. No discernible differences in surface features were observed on SEM images.

The results indicate that different cleaning methods affect the long-term light transmittance of the studied polypropylene/ethylene copolymer retainer material. However, for an individual cleaning method, no significant differences were shown for surface roughness or flexural modulus values at 6-months compared to baseline.