Destabilized Passivation Layer on Magnesium-Based Intermetallics as Potential Anode Active Materials for Magnesium...

Passivation of magnesium metal anode is one of the critical challenges for the development of magnesium batteries. Here we investigated the passivation process of an intermetallic anode: Mg₃Bi₂ synthesized by solid-state and thin film process. The Mg₃Bi₂ composite electrode shows excellent reversibility in magnesium bis(trifluoromethansulfonylamide) dissolved in acetonitrile, while Mg₃Sb₂, which has same crystal structure and similar chemical properties, is electrochemically inactive. We also fabricated the Mg₃Bi₂ thin film electrodes, which show reversibility with low overpotential not only in the acetonitrile solution but also glyme-based solutions. Surface layer corresponding to the decomposed TFSA anion is slightly suppressed in the case of the Mg₃Bi₂ thin film electrode, compared with Mg metal. Comparative study of hydrolysis process of the Mg₃Bi₂ and the Mg₃Sb₂ suggests that the both intermetallic anodes are not completely passivated. The bond valence sum mapping of the Mg₃Bi₂ indicates that the fast Mg²⁺ diffusion pathway between 2d tetrahedral sites is formed. The electrochemical properties of the Mg₃Bi₂ anode is mainly due to the less passivation surface with the fast Mg²⁺ diffusion pathways.