Inhibition of enamel demineralization by an ion-releasing tooth-coating material

To evaluate the inhibitory effect of a surface pre-reacted glass-ionomer (S-PRG) filler-containing tooth-coating material on enamel demineralization. The outer surface of the S-PRG filler is in a state in which ions are readily released.

Human enamel blocks were incubated in lactic acid solution (pH 4.0) with and without a disk (n=6) made of the cured tooth-coating material. Test solutions were changed every 24 hours and incubation was continued for 4 days. The pH and amount of fluoride released were measured with an electrode and ion meter, respectively. The concentrations of ions (aluminum, boron, calcium, phosphorus, silicon, sodium, and strontium) were measured by inductively coupled plasma atomic emission spectroscopy. The surface of the enamel block was observed with a scanning electron microscope.

Enamel demineralization was not observed in an enamel block incubated with a disk of the tooth-coating material. Ions released from S-PRG filler had an acid buffering action in the low pH lactic acid solution. However, in the enamel block-only solution showing high levels of calcium ion release, the degree of demineralization was correlated with morphological changes of the enamel surface.

Due to the buffering effects of the pre-reacted glass-ionomer surface by ion release, the S-PRG filler-containing tooth-coating material inhibited enamel demineralization by neutralizing the acidic environment at an early time point.