Development of nanofibrous collagen-grafted poly (vinyl alcohol)/gelatin/alginate scaffolds as potential skin substitute
Parisa Sobhanian1, Mohammad Khorram1, Seyedeh-Sara Hashemi2
1School of Chemical and Petroleum Engineering, Shiraz University, Shiraz, Iran.
Abstract:
The main objective of this work is to fabricate a nanofibrous scaffold to regenerate skin tissue. A scaffold composed of poly (vinyl alcohol)/gelatin/alginate was prepared using electrospinning method. To improve scaffold biocompatibility and wound healing properties, collagen, extracted from rat tail, was grafted on as-prepared nanofibers. The prepared scaffolds were characterized by SEM, FTIR, swelling ratio test, and water vapor transmission rate (WVTR) measurement. Cytotoxicity of the scaffolds against human fibroblasts and L929 (NCBI C161) cells were tested using direct and indirect methods, respectively. Fibroblast cell adhesion and proliferation on the scaffold were also investigated. Results of morphological studies showed that beadless nanofibers with 229 nm diameter were prepared. ATR-FTIR spectra of collagen grafted nanofiber mats confirmed presence of the collagen on their surface. Collagen grafted nanofibers showed higher swelling ratio than nanofibers without collagen graft. Collagen grafting decreased VWTR. Collagen grafting decreased both tensile strength and Young's modulus of the nanofibrous scaffolds while increased their elongation at break. MTT results showed that both scaffolds are biocompatible with higher cell viability for nanofibers with collagen grafting. Fibroblast cell culture on the scaffolds demonstrated that both of scaffolds have good cell viability and proliferation while collagen grafted scaffold showed better results.
Related Concept Videos
01:38Preparation of Alcohols via Substitution Reactions
Alcohols can be synthesized from alkyl halides via nucleophilic substitution reactions. The highly polar carbon-halogen bond in the substrate makes halide a good leaving group. The hydroxide ion or water can act as a nucleophile to take the place of halide and form an alcohol. The substitution reactions occur via two different reaction pathways, SN1 or SN2, depending on the nature of carbon attached to the halide.
Primary alcohols are synthesized from primary alkyl halides, and the...
02:58Cell Potential and Free Energy
Thermodynamics is the branch of physics dealing with the relationship between heat and other forms of energy. In an electrochemical cell, chemical energy is converted into electrical energy.
Thus, a link can be predicted between cell potential, free energy change, and the equilibrium constant for the reaction. Cell potential can also be measured as the oxidant or the reducing strength, and similar acid-base strength measures are reflected in equilibrium...
01:11Fibril-associated Collagen
For example, the type II collagen fibrils in cartilage have covalently bound type IX fibril-associated collagens at regular intervals. Other types of fibril-associated collagens are...
02:37Oxidation of Alcohols
The process of oxidation in a chemical reaction is observed in any of the three forms:
02:29Ethers from Alcohols: Alcohol Dehydration and Williamson Ether Synthesis
Ethers can be prepared from organic compounds by various methods. Some of them are discussed below,
Preparation of Ethers by Alcohol Dehydration
In this method, in the presence of protic acids, alcohol dehydrates to produce alkenes and ethers under different conditions. For example, in the presence of sulphuric acid, dehydration of ethanol at 413 K yields ethoxyethane, whereas it yields ethene at 443 K.
02:31Protection of Alcohols
Protection
It defines a protecting group as the masking agent to make the more reactive species inert to a given set of conditions. This concept is depicted via the illustration of liquid flow through different outlets in an assembly of pipes. The analogy helps to understand the role...