Flexible Mid-infrared Photonic Circuits for Real-time and Label-Free Hydroxyl Compound Detection

Chip-scale chemical detections were demonstrated by mid-Infrared (mid-IR) integrated optics made by aluminum nitride (AlN) waveguides on flexible borosilicate templates. The AlN film was deposited using sputtering at room temperature, and it exhibited a broad infrared transmittance up to λ = 9 µm. The AlN waveguide profile was created by microelectronic fabrication processes. The sensor is bendable because it has a thickness less than 30 µm that significantly decreases the strain. A bright fundamental mode was obtained at λ = 2.50-2.65 µm without mode distortion or scattering observed. By spectrum scanning at the -OH absorption band, the waveguide sensor was able to identify different hydroxyl compounds, such as water, methanol, and ethanol, and the concentrations of their mixtures. Real-time methanol monitoring was achieved by reading the intensity change of the waveguide mode at λ = 2.65 μm, which overlap with the stretch absorption of the hydroxyl bond. Due to the advantages of mechanical flexibility and broad mid-IR transparency, the AlN chemical sensor will enable microphotonic devices for wearables and remote biomedical and environmental detection.