Comprehensive Study on Chemical and Hot Press-Treated Silver Nanowires for Efficient Polymer Solar Cell Application

In this study, chemical treatment (CT; oxidation⁻reduction method) and physical treatment (HP; hot-pressing methods) were applied to improve the performance of silver nanowire (AgNW)-derived electrodes on a glass or flexible polyethylene terephthalate (PET) substrate. The four-point probe method, UV-Vis spectroscopy and scanning electron microscopy (SEM) were used to measure the properties of AgNW electrodes and compare them with those of indium tin oxide (ITO) electrodes for exploring the possibility of using CT- and HP-based AgNW electrodes for polymer solar cell (PSC) applications. Using the CT or HP method, the sheet resistance of electrodes decreased to lower than 40 Ω sq^-1 with an average high transmittance of more than 80%. Furthermore, HP reduced the surface roughness of AgNWs, which solved the inter-electrode short circuiting problem for devices. We studied the performance of poly(3,4-ethylenedioxythiophene)-poly(styrene sulfonate) and zinc oxide-based PSC devices. The power conversion efficiency of HP-AgNW-derived poly[4,8-bis(5-(2-ethylhexyl)thiophen-2-yl)benzo[1,2-b;4,5-b']dithiophene-2,6-diyl-alt-(4-(2-ethylhexyl)-3-fluorothieno[3,4-b]thiophene-)-2-carboxylate-2-6-diyl] (PTB7-Th):[6,6]-phenyl-C₇₁-butyric acid methyl ester (PC₇₁BM) devices was 7.83%, which was slightly lower than the performance of the device using ITO (8.03%) as a substrate. After a bend test (100 times) at a 2-cm curvature radius, the efficiency of AgNW/PET-derived PSCs was more than 70%. The performance of PSCs made with AgNWs and ITO electrodes is comparable, but the cost of using AgNWs for electrodes is much lower; therefore, HP-derived AgNWs demonstrate great potential for optoelectronic applications.