Preparation Methods of Polypropylene/Nano-Silica/Styrene-Ethylene-Butylene-Styrene Composite and Its Effect on...

Compared with traditional insulation materials, such as cross-linked polyethylene (XLPE), polypropylene (PP) is famous for its better recyclable and thermal properties, as well as its good electrical performance. However, the problem of poor impact strength has restricted the application of pure PP in high-voltage, direct current (HVDC) cables. In this paper, styrene-ethylene-butylene-styrene block copolymer (SEBS) was used as a toughening filler, and nano-SiO₂ was expected to improve the electric properties of the nano-composite. By controlling the masterbatch system, the dispersion characteristics of nano-SiO₂ in the ternary composite system were changed. When PP/SiO₂ was used as the masterbatch and then blended with SEBS, nano-SiO₂ tended to disperse in the PP phase, and the number of nano-particles in the SEBS phase was lower. When PP/SEBS was used as the masterbatch, nano-SiO₂ was distributed in both the PP phase and the SEBS phase. When SEBS/SiO₂ was used as the masterbatch, nano-SiO₂ tended to be dispersed in the SEBS phase. The different dispersion characteristics of nano-SiO₂ changed the crystallization and mechanical properties of the ternary composite system and produced different electrical performance improvement effects. The results of our experiment revealed that the space charge suppression capability was positively correlated with the direct current (DC) breakdown strength improvement effect. Compared with the DC performance of 500 kV commercial XLPE materials, the self-made PP-based ternary composite system has better space charge suppression effects and higher DC breakdown strength. When nano-SiO₂ was more dispersed in the PP phase, the space charge improvement effect was best. When the nano-SiO₂ particles were more dispersed in the SEBS phase, the expected electrical property improvement was not obtained. Scanning electron microscopy showed that the nano-SiO₂ particles in the SEBS phase were more dispersed at the interface than in the SEBS matrix, indicating that the nano-particles were poorly dispersed, which may be a reason why the electrical properties of the composite system were not significantly improved.