Thermal Conductivity of Molten Carbonates with Dispersed Solid Oxide from Differential Scanning Calorimetry

Recently, there has been a noticeable increase in the applications of composite mixtures containing molten salt and solid oxide for thermal energy conversion and storage systems. This highlights that thermal conductivity of the composites are central for the purpose of designing and devising processes. Measuring the thermal conductivity of molten samples at elevated temperatures remains challenging. In this study, the possibility to use heat flux differential scanning calorimetry (DSC) to measure the thermal conductivity of molten samples at elevated temperatures is reported for the first time. The thermal conductivity of composite mixtures containing eutectic (Li,Na)₂CO₃ with and without selected solid oxides at ~675 °C was determined by using the proposed DSC approach. This mixture is a candidate for high temperature waste heat conversion to electric energy. In the DSC measurement program, steps with repeated thermal cycles between 410 and 515 °C were included to limit the effect of the interface thermal contact resistance. The determined values 0.826 ± 0.001, and 0.077 ± 0.004 W m^-1K^-1 for the carbonate mixtures with and without solid MgO were found to match the reliable analysis at similar conditions.