Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior
Published on: June 27, 2018
Comparison of Self-Etching Ceramic Primer and Conventional Silanization to Bond Strength in Cementation of Fiber
Nan-Sim Pang1, Bock-Young Jung2, Byoung-Duck Roh3
1Department of Advanced General Dentistry, College of Dentistry, Yonsei University, Seoul 03722, Korea. pangns@yuhs.ac.
Abstract:
Various mechanical and chemical surface treatments have been proposed to improve the retention of fiber-reinforced composite post (FRCP), but the results are still controversial. The bond strength and durability of a self-etching ceramic primer, which was recently released as an alternative to etching and silane, are not yet known. This study aimed to compare and evaluate the push-out bond strength of different surface treatments of FRCPs after an artificial aging procedure. Four groups (n = 10) were established to evaluated FRCP surface treatments (dentin adhesive bonding; silane and adhesive bonding; hydrofluoric acid, silane and adhesive bonding; and a self-etching ceramic primer). They were bonded with dual-curing rein cement (Multilink N) and stored in distilled water at 37 °C for 30 days, then thermal cycled for 7500 cycles. After being sectioned into 1 mm thickness, each coronal and apical part was evaluated for its the push-out bond strength by a universal testing machine. Each debonded specimen was observed by an optical microscope and divided according to the failure modes. The results showed that silane treatment significantly improved push-out bond strength, but the self-etching ceramic primer did not do so. Additional hydrofluoric acid treatment or the adhesive bonding agent alone did not significantly improve the retention of FRCPs. Cohesive failure of the luting material was found most frequently in all groups.
More Related Videos
09:54Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process
Published on: June 30, 2023
06:26Experimental Implementation of a New Composite Fabrication Method: Exposing Bare Fibers on the Composite Surface by the Soft Layer Method
Published on: October 6, 2017
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:12Bonding and Strength of Aggregate
01:22Fiber Reinforced Concrete
02:49Bond Energies and Bond Lengths
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...