Silane reactivity and resin bond strength to lithium disilicate ceramic surfaces
Maria Dimitriadi1, Maria Zafiropoulou1, Spiros Zinelis1
1Department of Biomaterials, School of Dentistry, National and Kapodistrian University of Athens, Greece.
Objective:
To evaluate the silane status in commercially available products and their bonding capacity with polished glass-ceramic surfaces before and after hydrofluoric (HF) acid-etching.
Methods:
The products tested were Calibra Silane Coupling Agent/CS, G-Multi Primer/GM, Kerr Silane Primer/KS, Monobond Plus/MB and Scotchbond Universal Adhesive/SB. The silane status was studied by 13C nuclear magnetic resonance spectroscopy (13C-NMR). The roughness parameters of polished (group A) and HF acid-etched (group B) lithium disilicate glass-ceramic surfaces were measured by optical profilometry (n = 5/group). The interaction of the products with group A and B ceramic surfaces was examined by attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR). The shear strength (SBS) of a flowable composite bonded to the ceramic surfaces (groups A, B) was assessed before (NS) and after silane treatment (n = 20/group, product).
Results:
The NMR analysis showed the presence of silanol monomers only in CS. Methoxylated-siloxane adducts were found in GM, silanol-siloxane adducts in MB, SB, and siloxane polymers in KS. Acid-etching greatly increased Sa, Sz, Sdr, Sc and Sv parameters (p < 0.001) and ATR-FTIR analysis demonstrated evidence of bonding with the substrate in CS. Weibull analysis of SBS revealed the following rankings in characteristic life (p < 0.05): CS > SB,KS,MB > GM > NS (group A) and CS > GM > SB,KS,MB,NS (group B). The most reliable treatment in both groups was CS. For the same silane treatment, the SBS of group B were significantly higher from group A. Failures were mainly of adhesive type, except of several partial resin cohesive failures found in group B.
Significance:
The chemical bonding capacity of the silanes was highest in products with silanol monomers. Acid-etching increased bond strength to a level that neutralized the silane contribution in products with silanol-siloxane adducts and siloxane polymers, providing thus bond strength values similar to silane-free treatments.
More Related Videos
Related Concept Videos
01:12Bonding and Strength of Aggregate
02:49Bond Energies and Bond Lengths
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:48Ionic Bonding and Electron Transfer
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:43Peptide Bonds