Potential Reproducibility of Potassium-Selective Electrodes Having Perfluorinated Alkanoate Side Chain Functionalized...

The irreproducibility of the standard potential (E°) is probably the last major challenge for the commercialization of solid-contact ion-selective electrodes (SCISEs) as single-use or wearable sensors. To overcome this issue, we are introducing for the first time a perfluorinated alkanoate side chain functionalized poly(3,4-ethylenedioxythiophene) (PEDOTF) as a hydrophobic SC in potassium-selective electrodes (K-SCISEs) based on plasticized poly(vinyl chloride). The SC incorporates the tetrakis(pentafluorophenyl)borate (TFAB^-) anion, which is also present as a lipophilic additive in the ion-selective membrane (ISM), thus ensuring thermodynamic reversibility at the SC/ISM interface and improving the potential reproducibility of the electrodes. We show here that the PEDOTF-TFAB solid contact, which was prepolarized prior to the ISM deposition to either its half or fully conducting form (i.e. different oxidation states) in acetonitrile containing 0.01 M KTFAB, had a very stable open-circuit potential and an outstanding potential reproducibility of only ±0.5 mV (n = 6) for 1 h in the same solution after the prepolarization. This shows that the oxidation state of the highly hydrophobic PEDOTF-TFAB film (water contact angle 133°) is stable over time and can be precisely controlled with prepolarization. The SC was also not light sensitive, which is normally a disadvantage of conducting polymer SCs. After the ISM deposition, the standard deviation of the E° of the K-SCISEs prepared on glassy carbon was ±3.0 mV (n = 5), which is the same as that for conventional liquid contact K-ISEs. This indicates that the ISM deposition is the main source for the potential irreproducibility of the K-SCISEs, which has been overlooked previously.