In vitro evaluation of vascular endothelial cell behaviors on biomimetic vascular basement membranes

Vascular basement membrane (VBM) is a thin layer of fibrous extracellular matrix linking endothelium, and collagen type IV (COL IV) is its main composition. VBM plays a crucial role in anchoring down the endothelium to its loose connective tissue underneath. For vascular grafts, constructing biomimetic VBMs on the luminal surface is thus an effective approach to improve endothelialization in situ. In the present work, three types of polycaprolactone (PCL) membranes were produced and characterized through cell counting kit-8 (CCK-8) assay, adhesion force and elastic modulus test to examine the influence of fiber diameter and membrane composition on vascular endothelial cell (EC) behaviors. The PCL membranes with finer fibers of 54.77 nm (PCL-54) could biomimic the nanotopography of VBMs more efficiently than 544.64 nm (PCL-544), and they were more suitable for Pig iliac endothelium cells (PIECs) adhesion and proliferation, meanwhile, inducing higher elastic modulus and adhesion force of PIECs. On this foundation, we further immobilized COL IV onto PCL-54 (PCL-COL IV) to biomimic VBMs compositionally. Results showed that PIECs on PCL-COL IV exhibited the highest viability and proliferation. Besides, quantitative data indicated that the elastic modulus of the PIECs on PCL-COL IV (4441.00 Pa) was as two times higher than that on PCL-54 (2312.26 Pa), and the adhesion force grew to 1120.99 pN from 673.58 pN of PIECs on PCL-54. In summary, the PCL-COL IV membranes show high similarity with the native VBMs in terms of structure and composition, suggesting a promising potential for surface modification to vascular grafts for improved endothelialization.