Comparison of ISO and ASTM standards in determining the flexural strength of denture base resin

N Gopi Chander1, Venkatraman Jayaraman2, Venkat Sriram3

  • 1Research Scholar Department of Prosthodontics SRM Dental College, Ramapuram Chennai,India.

European Oral Research
|October 4, 2019
PubMed
Abstract

Keywords:
ASTMISOdenture basepoly methyl methacrylateresin

More Related Videos

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

680
Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives08:40

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives

Published on: May 17, 2020

3.3K

Related Concept Videos

Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
412
Flexural Stress01:16

Flexural Stress

When analyzing bending in symmetric members, it's crucial to understand how stresses distribute when subjected to bending moments. This stress distribution is effectively described by applying fundamental mechanics and material science principles, particularly Hooke's Law for elastic materials.
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
646
Bending of Members Made of Several Materials01:11

Bending of Members Made of Several Materials

In analyzing a structural member composed of two different materials with identical cross-sectional areas, it is crucial to understand how their distinct elastic properties affect the member's response under load. The analysis involves assessing stress and strain distributions using the transformed section concept, which accounts for variations in material properties.
Hooke's Law determines stress in each material, stating that stress is proportional to strain but varies due to each material's...
535
Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
988
Hooke's Law01:26

Hooke's Law

Hooke's law, a pivotal principle in material science, establishes that the strain a material undergoes is directly proportional to the applied stress, defined by a factor called the modulus of elasticity or Young's modulus.
1.4K
Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
429