Effect of a Self-Etch Adhesive Containing Nanobioglass on Postoperative Sensitivity of Posterior Composite
Ahmed Zakaria Aboelenein1, Mona Ismail Riad2, Mohammed Fouad Haridy2,3
1Operative Dentistry Department, Faculty of Dentistry, Fayoum University, Fayoum, Egypt.
Background:
Postoperative sensitivity is one of the major problems regarding posterior resin composite restorations that causes patient discomfort, maybe a reason for replacement of the restoration with an additional office time.
Aim:
To evaluate the effect of the addition of a Nanobioglass to a self-etch adhesive on the reduction of post-operative sensitivity following composite restorations versus a self-etch adhesive that is free of Nanobioglass agent.
Materials And Methods:
Sixteen patients having class II carious lesions were included in the study. After cavity preparation, each tooth was randomised to one of the following restorative treatments. Teeth in the control group were restored using self-etch adhesive (OptiBond All-In-One, Kerr) that is free of nanobioglass agent, and nano-hybrid resin composite (Herculite Ultra, Kerr). Restoration of teeth in the experimental group was similar to the control except that a nanobioglass agent was added to the self-etch adhesive. Patients were contacted for evaluation of postoperative sensitivity at 1 day, 1 week, 1 month, and 3 months. Data were analyzed using friedmann test followed by fisher exact test.
Results:
The experimental group (self-etch adhesive containing nanobioglass) showed a significantly less postoperative sensitivity compared with the control group (Self-etch adhesive free of nanobioglass) at 1 day, and 1-week evaluation periods. While both groups did not possess any significant difference at 1 month, and 3 months periods.
Conclusion:
The problem of postoperative sensitivity following resin composite restorations could be solved by the addition of bioglass nanoparticles into dental adhesives.