Influence of Contact Stress on Surface Microstructure and Wear Property of D2/U71Mn Wheel-Rail Material

Chun-Peng Liu1, Xiu-Juan Zhao2,3, Peng-Tao Liu4,5

  • 1School of Material Science and Engineering, Dalian Jiaotong University, Dalian 116028, China. liuchunpeng1991@sina.com.

Materials (Basel, Switzerland)
|October 11, 2019
PubMed

Keywords:
D2 wheel steelU71Mn rail steelcontact stressfatigue wearsurface microstructure

More Related Videos

Preparation and High-temperature Anti-adhesion Behavior of a Slippery Surface on Stainless Steel10:52

Preparation and High-temperature Anti-adhesion Behavior of a Slippery Surface on Stainless Steel

Published on: March 29, 2018

7.9K
Knowledge Based Cloud FE Simulation of Sheet Metal Forming Processes11:05

Knowledge Based Cloud FE Simulation of Sheet Metal Forming Processes

Published on: December 13, 2016

12.6K

Related Concept Videos

Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
1.8K
Dry Friction01:30

Dry Friction

Dry friction occurs between two solid surfaces in contact as they attempt to move relative to one another. In daily life, dry friction is encountered in various forms, such as when walking on the ground, sliding an object across a table, or rubbing hands together. Despite its ubiquity, the underlying mechanisms behind dry friction are not readily visible.
To illustrate this concept, imagine a wooden crate resting on a rough, non-uniform horizontal surface. When an external force is applied to...
870
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
446
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
462
Bearing Stress01:22

Bearing Stress

Bearing stress refers to the contact pressure between two separate bodies. To visualize this, imagine a bolt thrust through a plate. The bolt applies a force to the plate, which exerts an equal but opposite force back onto the bolt. This force isn't just a singular entity but a compilation of numerous smaller forces distributed across the contact surface between the bolt and the plate.
Due to the intricacy of these microforces, an average value, known as bearing stress, is often used by...
1.8K
Rolling Resistance01:21

Rolling Resistance

When a solid cylinder rolls steadily on a rigid surface, the normal force applied by the surface on the cylinder is perpendicular to the tangent at the contact point. However, since no materials are entirely rigid, the surface's reaction to the cylinder involves a range of normal pressures.
For instance, imagine a hard cylinder rolling on a comparatively soft surface. The cylinder's weight compresses the surface beneath it. As the cylinder moves, the material in front of it slows down due to...
580