Tailoring Surface Hydrophilicity Property for Biomedical 316L and 304 Stainless Steels: A Special Perspective on...

Stainless steels used as metal implants in the medical field have been attracting intensive attention due to their advantages in mechanical properties, anticorrosion properties, and cost effectiveness. Good osteoconductivity, low toxicity, and low inflammatory reactions are essential to stainless steel implant in vivo. However, there are few cases about the surface modification performed for enhancing the corrosion resistance, and there are few researches on the relationship between the surface properties of stainless steel and osteoconductivity when used as implants. This study employed 316L and 304 stainless steel for surface modification including hydrothermal treatment after acid immersion and anodizing treatment, while the as-polished stainless steel was used as a control group. Anticorrosion properties, protein adsorption properties, osteoconductivity, and anti-inflammation property of these specimens were intensively investigated in vitro and in vivo. It was found that specimen subjected to hydrothermal treatment at 230 °C after immersion in 18 M H₂SO₄ had the lowest metal ions release, while the anodized specimen had the highest release of Fe and Cr due to corrosion. The protein adsorption amount of the specimens was positively related to the osteoconductivity, suggesting protein adsorption is the prerequisite for good osteoconductivity. The osteoconductivity decreased first and then increased with the increase in water contact angle (WCA) value. The specimen with the surface modified by hydrothermal treatment after acid immersion had the highest protein adsorption amount and the best osteoconductivity due to its superhydrophilicity property. The protein adsorption capacity and osteoconductivity for stainless steel tended to be the same as Ti alloys studied before, indicating the surface hydrophilicity property of the implanted metals was the dominant factor affecting the osteoconductivity. From an anti-inflammation perspective, the specimen with the surface modified by hydrothermal treatment after acid immersion also exhibited the lowest thickness of the fibrous capsule membrane from the in vivo tests, suggesting its advantageous biocompatibility. Thus, this research can provide new insight into the application of austenitic stainless steel for implanted material purposes.