Spectroscopic and Electrical Characterizations of Low-Damage Phosphorous-Doped Graphene via Ion Implantation

Development of n-/p-type semiconducting graphenes is a critical route to implement in graphene-based nanoelectronics and optronics. Compared to the p-type graphene, the n-type graphene is more difficult to be prepared. Recently, phosphorous doping was reported to achieve air-stable and high mobility of n-typed graphene. The phosphorous-doped graphene (P-Gra) by ion implantation is considered as an ideal method for tailoring graphene due to its IC compatible process; however, for a conventional ion implanter, the acceleration energy is in the order of kiloelectron volts (keV), thus severely destroys the sp² bonding of graphene owing to its high energy of accelerated ions. The introduced defects, therefore, degrade the electrical performance of graphene. Here, for the first time, we report a low-damage n-typed chemical vapor deposition (CVD) graphene by an industrial-compatible ion implanter with an energy of 20 keV where the designed protection layer (thin Au film) covered on as-grown CVD graphene is employed to efficiently reduce defect formation. The additional post-annealing is found to heal the crystal defects of graphene. Moreover, this method allows transferring ultraclean and residue-free P-Gra onto versatile target substrates directly. The doping configuration, crystallinity, and electrical properties on P-Gra were comprehensively studied. The results indicate that the low-damaged P-Gra with a controllable doping concentration of up to 4.22 at % was achieved, which is the highest concentration ever recorded. The doped graphenes with tunable work functions (4.85-4.15 eV) and stable n-type doping while keeping high-carrier mobility are realized. This work contributes to the proof-of-concept for tailoring graphene or 2D materials through doping with an exceptional low defect density by the low energy ion implantation, suggesting a great potential for unconventional doping technologies for next-generation 2D-based nanoelectronics.