Adhesive Joint Stiffness in the Aspect of FEM Modelling

The paper presents the results of nanoindentation testing, carried out along the thickness of the adhesive joint joining sheets of aluminum alloy. The purpose of the tests was to determine changes in the Young's modulus in the joint resulting from the active impact of the joined aluminum alloy sheets on the adhesive during curing of the adhesive bond. Structural changes that take place during curing of the joint, especially in the boundary zone, can have a significant impact on the adhesive properties and consequently, on the adhesive joint strength. The Young's modulus of the adhesive (Ek) in the joint assumes variable values as the distance from the connections changes. This phenomenon is called the apparent Young's modulus. The problem is to define the size of the boundary zone in which the value of Ek significantly differs from the value in the so-called core. Based on the obtained results of experimental tests, a numerical model was built taking into account the observed differences in the properties of the joint material. The stress distribution in the adhesive joint, single-lap connection with the three-zone adhesive joint, was analyzed in comparison to the classical numerical model in which adhesive in the adhesive joint is treated as isotropic in terms of rigidity.