Chemical composition and roughness of enamel and composite after bleaching, acidic beverages and toothbrushing
Marília-de-Morais Pinelli1, Anderson Catelan2,3, Luís-Felipe-Marques de Resende1
1Graduate Student, Department of Dentistry, University of Taubaté, Taubaté, SP, Brazil.
Background:
In this study was assessed the surface roughness and chemical composition of tooth enamel and composite resin after bleaching treatment, immersion in acidic beverages, and simulated toothbrushing.
Material And Methods:
One hundred and twenty dental blocks (10 x 10 x 3 mm) were randomly assigned (n = 10) according to surface treatment [none (N), bleaching (B), toothbrushing (T), and B+T] and storage medium [saliva (S), whiskey (W), and orange juice (O)]: experimental groups - N+S, N+W, N+O, B+S, B+W, B+O, S+T, W+T, O+T, B+S+T, B+W+T, and B+O+T. Two bleaching sessions were conducted using 38% hydrogen peroxide (3 applications). Surface roughness was measured using a roughness tester and composition was determined by micro energy-dispersive X-ray fluorescence spectrometry (µ-EDXRF) before and after treatments. Calcium/phosphorus (Ca/P) ratio in enamel and silica (Si) content in composite were evaluated. Data were statistically analyzed by ANOVA and Tukey's test (α = 0.05).
Results:
Overall, increased values of surface roughness for enamel and composite were observed mainly after immersion in orange juice and bleaching/toothbrushing association. Moreover, this association and immersion in whiskey resulted in lower Ca/P ratio and after aging methods, bleached and bleached/toothbrushed groups showed decreased in Ca/P ratio compared to initial values. All groups showed Si content decrease at the end, except the group without surface treatment and immersed in saliva, and bleaching followed by immersion in orange juice and toothbrushing caused the highest Si reduction.
Conclusions:
Bleaching and toothbrushing combination strengthened the effects caused by acidic drinks on roughness and chemical composition of enamel and composite. Key words:Tooth bleaching, toothbrushing, physical properties, chemical properties.
Related Concept Videos
01:21Tooth Anatomy
The Crown, Neck, and Root
The visible part of the tooth is referred to as the crown. It's covered by enamel, the hardest substance in the human body. The crown is uniquely shaped for each type of tooth, allowing for different functions such as cutting, tearing, or...
01:18Titration of Polyprotic Base with a Strong Acid
01:21Acid Attack on Concrete
The rate at which hydrogen...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
03:27Mixtures of Acids
A Mixture of a Strong Acid and a Weak Acid
In a mixture of a strong acid and a weak acid, the strong acid dissociates completely and becomes a source of almost all the hydronium ions...
01:19Mixtures of Acids
In a strong and weak acid mixture, the strong acid dissociates completely and becomes a source of almost all the hydronium ions present in the solution. In contrast, the weak acid shows...