Polymorphism of Bismuth Sesquioxide. II. Effect of Oxide Additions on the Polymorphism of Bi₂O₃

The effect of small oxide additions on the polymorphism of Bi₂O₃ was studied by means of high-temperature x-ray diffractometry. Solidus and occasional liquidus temperatures were approximated, so that tentative partial phase diagrams for 33 oxide additions were constructed. Only the monoclinic and the cubic forms of Bi₂O3 were found to be stable. Other phases, frequently reported by previous investigators, such as tetragonal and body-centered cubic (b.c.c.), were shown to form metastably from cooled liquid or cubic. An impure b.c.c. phase of distinct but variable composition appeared in systems of ZnO, PbO, B₂O₃, Al₂O₃, Ga₂O₃, Fe₂O₃, SiO₂, GeO₂, TiO₂, and P₂O₅. The impure b.c.c. phase in the systems with SiO₂, GeO₂, and TiO₂ melted congruently about 100 °C above the m.p. of Bi₂O₃. The impure b.c.c. phase was formed metastably in systems with Rb₂O, NiO, MnO, CdO, V₂O₅, and Nb₂O₅; the conditions of formation were dependent on composition, preparation, and heating schedules. The impure b.c.c. phases, both stable and metastable, had smaller unit cell dimensions than that of pure Bi₂O₃.