Tuning Internal Strain in Metal-Organic Frameworks via Vapor Phase Infiltration for CO₂ Reduction

A gas-phase approach to form Zn coordination sites on metal-organic frameworks (MOFs) by vapor-phase infiltration (VPI) was developed. Compared to Zn sites synthesized by the solution-phase method, VPI samples revealed approximately 2.8 % internal strain. Faradaic efficiency towards conversion of CO₂ to CO was enhanced by up to a factor of four, and the initial potential was positively shifted by 200-300 mV. Using element-specific X-ray absorption spectroscopy, the local coordination environment of the Zn center was determined to have square-pyramidal geometry with four Zn-N bonds in the equatorial plane and one Zn-OH₂ bond in the axial plane. The fine-tuned internal strain was further supported by monitoring changes in XRD and UV/Visible absorption spectra across a range of infiltration cycles. The ability to use internal strain to increase catalytic activity of MOFs suggests that applying this strategy will enhance intrinsic catalytic capabilities of a variety of porous materials.