Facilitating Lithium-Ion Diffusion in Layered Cathode Materials by Introducing Li+/Ni2+ Antisite Defects for
Zhongfeng Tang1, Sen Wang2, Jiaying Liao1
1CAS Key Laboratory of Materials for Energy Conversions, Department of Materials Science and Engineering & Collaborative Innovation Center of Suzhou Nano Science and Technology, University of Science and Technology of China, Anhui Hefei 230026, China.
Abstract:
Li+/Ni2+ antisite defects mainly resulting from their similar ionic radii in the layered nickel-rich cathode materials belong to one of cation disordering scenarios. They are commonly considered harmful to the electrochemical properties, so a minimum degree of cation disordering is usually desired. However, this study indicates that LiNi0.8Co0.15Al0.05O2 as the key material for Tesla batteries possesses the highest rate capability when there is a minor degree (2.3%) of Li+/Ni2+ antisite defects existing in its layered structure. By combining a theoretical calculation, the improvement mechanism is attributed to two effects to decrease the activation barrier for lithium migration: (1) the anchoring of a low fraction of high-valence Ni2+ ions in the Li slab pushes uphill the nearest Li+ ions and (2) the same fraction of low-valence Li+ ions in the Ni slab weakens the repulsive interaction to the Li+ ions at the saddle point.