A New Ultra-High-Strength AB83 Alloy by Combining Extrusion and Caliber Rolling

An exceptionally high-strength rare-earth-free Mg-8Al-3Bi (AB83) alloy was successfully fabricated via extrusion and caliber rolling. After three-pass caliber rolling, the homogenous microstructure of the as-extruded AB83 alloy was changed to a necklace-like bimodal structure consisting of ultra-fine dynamic recrystallized (DRXed) grains and microscale deformed grains. Additionally, both Mg₁₇Al₁₂ and Mg₃Bi₂ nanoprecipitates, undissolved microscale Mg₁₇Al₁₂, and Mg₃Bi₂ particles were dispersed in the matrix of caliber-rolled (CRed) AB83 alloy. The CRed AB83 sample demonstrated a slightly weakened basal texture, compared with that of the as-extruded sample. Consequently, CRed AB83 showed a tensile yield strength of 398 MPa, an ultimate tensile strength of 429 MPa, and an elongation of 11.8%. The superior mechanical properties of the caliber-rolled alloy were mainly originated from the combined effects of the necklace-like bimodal microstructure containing ultra-fine DRXed grains, the homogeneously distributed nanoprecipitates and microscale particles, as well as the slightly modified basal texture.