Injectable phosphopullulan-functionalized calcium-silicate cement for pulp-tissue engineering: An in-vivo and ex-vivo
Mariano Simón Pedano1, Xin Li2, Bernardo Camargo3
1KU Leuven (University of Leuven), Department of Oral Health Sciences, BIOMAT & UZ Leuven (University Hospitals Leuven), Dentistry, Leuven, Belgium.
Objective:
To evaluate, by means of an ex-vivo human tooth-culture model and in-vivo minipig animal study, the pulpal inflammatory reaction and reparative dentin-formation capacity of an injectable phosphopullulan-based calcium-silicate cement (GC, Tokyo, Japan) upon pulp capping, this in comparison with the commercial reference material Biodentine (Septodont).
Methods:
For the ex-vivo tooth model, 9 freshly-extracted teeth from 3 different patients were pulp-capped with the experimental biomaterial (n = 3), Biodentine (n = 3) or left uncapped (control; n = 3). The teeth were kept in fresh culture medium for 4 weeks and, upon fixation three-dimensional Micro-CT and histology were performed. For the in-vivo animal study, 40 teeth from 3 minipigs were exposed and pulp capped with the experimental biomaterial containing phosphopullulan (n = 24) or Biodentine (n = 16) for 7 or 70 days. The inflammatory reaction and the tissue-regenerative potential was qualitatively and semi-quantitatively characterized using three-dimensional micro-CT and histology.
Results:
Ex vivo, the treatment with the experimental phosphopullulan-based calcium-silicate cement and Biodentine stimulated the formation of fibrous tissue and mineralized foci. In vivo, early inflammatory reaction and regeneration of the pulp-tissue interface was promoted by both bioceramic materials after 7 and 70 days, respectively.
Significance:
Our findings bring new insights into calcium-silicate-mediated dental pulp repair and regeneration. The novel ready-to-use and self-adhering functionalized calcium-silicate cement revealed effective pulpal repair potential.