High-Temperature Oxidation of Heavy Boron-Doped Diamond Electrodes: Microstructural and Electrochemical Performance...

In this work, we reveal in detail the effects of high-temperature treatment in air at 600 °C on the microstructure as well as the physico-chemical and electrochemical properties of boron-doped diamond (BDD) electrodes. The thermal treatment of freshly grown BDD electrodes was applied, resulting in permanent structural modifications of surface depending on the exposure time. High temperature affects material corrosion, inducing crystal defects. The oxidized BDD surfaces were studied by means of cyclic voltammetry (CV) and scanning electrochemical microscopy (SECM), revealing a significant decrease in the electrode activity and local heterogeneity of areas owing to various standard rate constants. This effect was correlated with a resultant increase of surface resistance heterogeneity by scanning spreading resistance microscopy (SSRM). The X-ray photoelectron spectroscopy (XPS) confirmed the rate and heterogeneity of the oxidation process, revealing hydroxyl species to be dominant on the electrode surface. Morphological tests using scanning electron microscopy (SEM) and atomic force microscopy (AFM) revealed that prolonged durations of high-temperature treatment lead not only to surface oxidation but also to irreversible structural defects in the form of etch pits. Our results show that even subsequent electrode rehydrogenation in plasma is not sufficient to reverse this surface oxidation in terms of electrochemical and physico-chemical properties, and the nature of high-temperature corrosion of BDD electrodes should be considered irreversible.