Enhanced Electrical Conductivity and Seebeck Coefficient in PEDOT:PSS via a Two-Step Ionic liquid and NaBH4 Treatment
Jonathan Atoyo1, Matthew R Burton1, James McGettrick1
1SPECIFIC-IKC, Materials Research Centre, College of Engineering, Swansea University, Bay Campus, Swansea SA1 8EN, UK.
Abstract:
A two-step approach of improving the thermoelectric properties of Poly(3,4-ethylenedioxythiophene)poly(4-styrenesulfonate) (PEDOT:PSS) via the addition of the ionic liquid, 1-Ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (EMIM:TFSI) and subsequent reduction with NaBH4 is presented. The addition of 2.5 v/v% of EMIM:TFSI to PEDOT:PSS increases the electrical conductivity from 3 S·cm-1 to 1439 S·cm-1 at 40 °C. An additional post treatment using the reducing agent, NaBH4, increases the Seebeck coefficient of the film from 11 µV·K-1 to 30 µV·K-1 at 40 °C. The combined treatment gives an overall improvement in power factor increase from 0.04 µW·m-1·K-2 to 33 µW·m-1·K-2 below 140 °C. Raman and XPS measurements show that the increase in PEDOT:PSS conductivity is due to PSS separation from PEDOT and a conformational change of the PEDOT chains from the benzoid to quinoid molecular orientation. The improved Seebeck coefficient is due to a reduction of charge carriers which is evidenced from the UV-VIS depicting the emergence of polarons.