The influence of temperature and component proportion on stability, sensitivity, and mechanical properties of...

Based on molecular dynamics (MD) simulation, the binding energy, cohesive energy density (CED), bond length, and mechanical parameters were calculated for 2,6-diamino-3,5-dinitropyrazine-l-oxide (LLM-105) crystal, octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine (HMX) crystal, and their co-crystals under different temperatures. Three LLM-105/HMX patterns were constructed to investigate the influence of component proportion on structures and properties of co-crystals, in which the mole ratios of LLM-105 and HMX are 1:1, 1:2, and 2:1. The effect of temperature and components on the stability and sensitivity were investigated as well. The results show that the binding energies, CED and mechanical parameters of all the co-crystals, decrease when the temperature increases from 248 to 398 K, while their maximum N-NO₂ bond length (L_max) increases with rising temperature, indicating that the sensitivities increase and stabilities decrease when temperature rises. At all temperatures, co-crystals exhibit larger CED and shorter bond length than that of single explosive, demonstrating that they are more stable and less sensitive than single crystal, where the stability of co-crystals was ordered as 2:1>1:1>1:2. Moreover, the bulk modulus (K) and shear modulus (G) of co-crystals are lower than that of HMX, conversely, the Cauchy pressure and K/G are higher than that of HMX, implying co-crystals have better ductility. Finally, the 2:1 ratio of LLM-105/HMX co-crystal was identified as the excellent one, owning to the highest binding energy, highest CED, shortest L_max, and greatest ductility. Graphical Abstract Models of LLM-105/HMX and one of the properties.