Renewable Fabric Surface-Initiated ATRP Polymerizations: Towards Mixed Polymer Brushes

Wojciech Raj1, Alessandro Russo2, Yaoming Zhang1,3

  • 1Lodz University of Technology, Institute of Polymer and Dye Technology, Stefanowskiego 12/16, 90-924 Lodz, Poland.

Nanomaterials (Basel, Switzerland)
|March 21, 2020
PubMed

Keywords:
mixed polymer brushessurface modificationsurface thermal rearrangement

More Related Videos

Fabricating Reactive Surfaces with Brush-like and Crosslinked Films of Azlactone-Functionalized Block Co-Polymers10:09

Fabricating Reactive Surfaces with Brush-like and Crosslinked Films of Azlactone-Functionalized Block Co-Polymers

Published on: June 30, 2018

8.6K
Preparation and Friction Force Microscopy Measurements of Immiscible, Opposing Polymer Brushes13:57

Preparation and Friction Force Microscopy Measurements of Immiscible, Opposing Polymer Brushes

Published on: December 24, 2014

14.3K

Related Concept Videos

Anionic Chain-Growth Polymerization: Overview01:20

Anionic Chain-Growth Polymerization: Overview

The polymerization process that involves carbanion as an intermediate is called anionic polymerization. It is also a type of addition or chain-growth polymerization. Anionic polymerization gets initiated by a strong nucleophile such as an organolithium or a Grignard reagent. The most commonly used initiator for anionic polymerization is butyl lithium. Monomers involved in anionic polymerization must possess a vinyl group bonded to one or two electron-withdrawing groups. For instance,...
2.4K
Types of Step-Growth Polymers: Polyesters01:20

Types of Step-Growth Polymers: Polyesters

The introduction of polyesters has brought major development to the textile industry. The wrinkle-free behavior of polyester blends has eliminated the need for starching and ironing clothes.
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the polymer...
2.5K
Cationic Chain-Growth Polymerization: Mechanism00:57

Cationic Chain-Growth Polymerization: Mechanism

The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the...
2.7K
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
4.2K
Radical Chain-Growth Polymerization: Mechanism01:09

Radical Chain-Growth Polymerization: Mechanism

The radical chain-growth polymerization mechanism consists of three steps: initiation, propagation, and termination of polymerization. The polymerization initiates when a free radical generated from the radical initiator adds to the unsaturated bond in the monomer. The unpaired electron of the free radical and one π electron in the unsaturated bond creates a σ bond between the free radical and the monomer. As a result, the other π electron in the unsaturated bond converts this species into...
3.2K
Free-Radical Chain Reaction and Polymerization of Alkenes02:35

Free-Radical Chain Reaction and Polymerization of Alkenes

The conversion of alkenes to macromolecules called polymers is a reaction of high commercial importance. The structure of the polymer is defined by a repeating unit, while the terminal groups are considered insignificant. The average degree of polymerization represents the number of repeating units in the polymer molecule and is denoted by the subscript n.