Role of Underlayer for Efficient Core-Shell InGaN QWs Grown on m-plane GaN Wire Sidewalls
Akanksha Kapoor1, Sylvain Finot2, Vincent Grenier1
1Université Grenoble Alpes, CEA, IRIG, PHELIQS, NPSC, Grenoble 38000, France.
Abstract:
Different types of buffer layers such as InGaN underlayer (UL) and InGaN/GaN superlattices are now well-known to significantly improve the efficiency of c-plane InGaN/GaN-based light-emitting diodes (LEDs). The present work investigates the role of two different kinds of pregrowth layers (low In-content InGaN UL and GaN UL namely "GaN spacer") on the emission of the core-shell m-plane InGaN/GaN single quantum well (QW) grown around Si-doped c̅-GaN microwires obtained by silane-assisted metal organic vapor phase epitaxy. According to photo- and cathodoluminescence measurements performed at room temperature, an improved efficiency of light emission at 435 nm with internal quantum efficiency >15% has been achieved by adding a GaN spacer prior to the growth of QW. As revealed by scanning transmission electron microscopy, an ultrathin residual layer containing Si located at the wire sidewall surfaces favors the formation of high density of extended defects nucleated at the first InGaN QW. This contaminated residual incorporation is buried by the growth of the GaN spacer and avoids the structural defect formation, therefore explaining the improved optical efficiency. No further improvement is observed by adding the InGaN UL to the structure, which is confirmed by comparable values of the effective carrier lifetime estimated from time-resolved experiments. Contrary to the case of planar c-plane QW where the improved efficiency is attributed to a strong decrease of point defects, the addition of an InGaN UL seems to have no influence in the case of radial m-plane QW.
Related Concept Videos
Metal-Semiconductor Junctions
Schottky Barriers
Schottky barriers arise when a metal with a work function (Φm) contacts a semiconductor with a different work function (Φs). Initially, electrons transfer until the Fermi levels of the metal and semiconductor align at equilibrium. For instance, if Φm > Φs, the semiconductor Fermi level is higher than the metal's before contact. The...
Biasing of Metal-Semiconductor Junctions
In Schottky junctions, where the semiconductor is n-type, applying a positive voltage to the metal relative to the semiconductor reduces its Fermi...
P-N junction
Biasing of P-N Junction
In equilibrium, no external voltage is applied across the p-n junction. The depletion region is formed at the junction interface due to the diffusion of carriers, which leaves behind charged dopants, acceptors on the p-side, and donors on the n-side. These immobile charges create an electric field that prevents further diffusion of carriers. The related energy band...