Synthesis of Poly(2-aminothiazole)-Coated Polystyrene Particles and Their Excellent Hg(II) Adsorption Properties

Synthesis of conjugated polymer-coated latex particles is an effective method to improve the poor processability of conjugated polyheterocycles. The key to success is to control the overlayer thickness so it is less than the size of the solvated layer of polymeric stabilizer. This paper presents a protocol to coat polymer latex particles with poly(2-aminothiazole) (PAT), which is a relatively new heterocyclic conjugated polymer. The protocol is based on chemical oxidative polymerizations of 2-aminothiazole using copper chloride as the oxidant at a fixed oxidant/monomer molar ratio of 0.5 in aqueous media in the presence of poly(N-vinyl-2-pyrrolidone)-functionalized polystyrene (PS) latex. The effects of monomer concentration, PS concentration, and polymerization temperature on the morphology of the PAT-coated PS composite particles were investigated by SEM and TEM, and the resulting composite particles characterized by FTIR and XPS. Optimization of the initial monomer concentration allowed colloidally stable PAT-coated PS composite particles to be formed at ambient temperature, and the PAT loading was easily adjusted by varying the initial PS concentration. The Hg(II) adsorption properties of selected PAT-coated PS composite particles were assessed preliminarily. The maximum adsorption capacity at 25 °C reached 440.25 mg/g, which is much higher than many other adsorbents.