Published on: April 26, 2017
Metallic Glass Films with Nanostructured Periodic Density Fluctuations Supported on Si/SiO2 as an Efficient Hydrogen
Baran Sarac1, Yurii P Ivanov2,3, Tolga Karazehir4
1Erich Schmid Institute of Materials Science, Austrian Academy of Sciences, 8700, Leoben, Austria.
Abstract:
Nanostructured metallic glass films (NMGF) can exhibit surface and intrinsic effects that give rise to unique physical and chemical properties. Here, a facile synthesis and electrochemical, structural, and morphologic characterization of Pd-Au-Si based MGs of approximately 50 nm thickness supported on Si/SiO2 is reported. Impressively, the maximum total hydrogen charge stored in the Pd-Au-Si nanofilm is equal to that in polycrystalline Pd films with 1 μm thickness in 0.1 m H2 SO4 electrolyte. The same NMGF has a volumetric desorption charge that is more than eight times and 25 % higher than that of polycrystalline PdNF and Pd-Cu-Si NMGF with the same thickness supported on Si/SiO2 , respectively. A significant number of nanovoids originating from PdHx crystals, and an increase in the average interatomic spacing is detected in Pd-Au-Si NMGF by high-resolution TEM. Such a high amount of hydrogen sorption is linked to the unique density fluctuations without any chemical segregation exclusively observed for this NMGF.
More Related Videos
08:45Integration of Light Trapping Silver Nanostructures in Hydrogenated Microcrystalline Silicon Solar Cells by Transfer Printing
Published on: November 9, 2015
12:08Fabrication of High Contrast Gratings for the Spectrum Splitting Dispersive Element in a Concentrated Photovoltaic System
Published on: July 18, 2015