Effect of Different Compatibilizers on the Properties of Poly (Lactic Acid)/Poly (Butylene Adipate-Co-Terephthalate)...

In this report, poly(lactic acid) (PLA) and Poly(butylene adipate-co-terephthalate) (PBAT) with three kinds of compatibilizers were melt blended under intensive shear flow. A self-made parallel three-screw extruder was developed to generate such flow during the process. Mechanical properties, chemical reactions among PLA, PBAT and compatibilizers, rheological behavior and morphology were investigated. The mechanical tests showed that the notched impact strength of super-tough composite with 10 wt% EGMA is about 20 times than that of pure PLA. The Fourier transform infrared spectroscopy (FT-IR) results showed that the epoxy functional groups or maleic anhydride functional groups of KT-20, KT-915 and EGMA reacted with the hydroxyl groups of PLA or PBAT macromolecules, resulting in a bridge of PLA and PBAT. About rheological properties, the tan δ-angular frequency curves and the η''- η' curves confirmed the chemical reactions mentioned above and indicated better compatibility of η''- η' between PLA and PBAT, respectively. Meanwhile, the loss modulus and storage modulus-angular frequency curves demonstrated the discrepancy of different compatibilizer components. In particular, from scanning electron microscopy (SEM) images, it can be seen that the phase size and dispersion uniformity of PBAT adjusted by compatibilizer, corresponding to better compatibility that is described in the η''- η' curves. The approach for producing super-tough PLA/PBAT/compatibilizer by intensive shear flow provides a viable direction for further improving PLA performance.