Electrochemical reduction of nitrate on boron-doped diamond electrodes: Effects of surface termination and...

This study is among the first to systematically study the electrochemical reduction of nitrate on boron-doped diamond (BDD) films with different surface terminations and boron-doping levels. The highest nitrate reduction efficiency was 48% and the highest selectivity in the production of nitrogen gas was 44.5%, which were achieved using a BDD electrode with a hydrogen-terminated surface and a B/C ratio of 1.0%. C-H bonds served as the anchor points for attracting NO₃^- anions close to the electrode surface, and thus accelerating the formation of NO₃^-_(ads). Compared to oxygen termination, hydrogen-terminated BDD exhibited higher electrochemical reactivity for reducing nitrate, resulting from the formation of shallow acceptor states and small interfacial band bending. The hydrophobicity of the hydrogen-terminated BDD inhibited water electrolysis and the subsequent adsorption of atomic hydrogen, leading to increased selectivity in the production of nitrogen gas. A BDD electrode with a boron-doping level of 1.0% increased the density of acceptor states, thereby enhancing the conductivity and promoting the formation of C-H bonds after the cathodic reduction pretreatment leading to the direct reduction of nitrate.