Lattice dynamics calculations and high-pressure Raman spectra of the ZnMoO₄

We report here the analysis of vibrational properties of the ZnMoO4 by using theoretical and experimental approaches, well as results of high pressure experiments in this system. The analysis of the lattice dynamics calculations through the classical rigid ion model, was applied to determine the mode assignment in the triclinic phase of the ZnMoO₄. Additionally, the experimental high-pressure Raman spectra of the ZnMoO₄ were carried out from 0 GPa up to 6.83 GPa to shed light on the structural stability of this system. The pressure-dependent studies showed that this crystal undergoes a first order phase transition at around 1.05 GPa. The Raman spectrum analysis of the new phase shows a significant change in the number of modes for the spectral range of 20-1000 cm^-1. The instability of this phase occurs due to the decrease of the MoO bond lengths in the high-pressure phase, connected with tilting and/or rotations of the MoO₄ tetrahedra leading to a disorder at the MoO₄ sites. The second and third phase transformations were observed, respectively, at about 2.9 GPa and 4.77 GPa, with strong evidences, in the Raman spectra, of crystal symmetry change. The principal component analysis (PCA) and the hierarchical cluster analysis (HCA) were used in order to infer the intervals of pressure where the different phases do exist. Discussion about the number of non equivalent sites for Mo ions and the kind of coordination for molybdenum atoms is also furnished.