Antimicrobial Activity of Nano-Magnesium Hydroxide Against Oral Bacteria and Application in Root Canal Sealer

BACKGROUND The goal of the present work was to assess the antibacterial activity of nano-magnesium hydroxide (NMH) against Streptococcus mutans (S. mutans) and to explore the antimicrobial function of AH Plus™ sealer incorporating NMH. MATERIAL AND METHODS The antimicrobial behavior of NMH against S. mutans was evaluated with bactericidal tests. A modified direct contact test was used to assess the antimicrobial activity of unset AH Plus containing NMH after 5 minutes, 20 minutes, and 60 minutes of contact with bacteria. The antimicrobial effects and the amount of surface-adhering bacteria of the solidified materials were explored by SEM and confocal laser scanning microscopy, respectively. RESULTS NMH powder presented excellent antimicrobial activity against S. mutans. Mg²⁺ and OH⁻ were not the main factors resulting in bacterial death. Approximately 93.1% and 98% of the S. mutans were killed in the AH Plus+7% NMH group after incubation for 5 minutes and 20 minutes, respectively. AH Plus with 5% or 7% NMH were more potent against S. mutans compared with AH Plus alone (P<0.05). Moreover, the antibacterial function of AH Plus was lost after setting. NMH enabled the solidified AH Plus to still have antibacterial properties on the seventh day. CONCLUSIONS NMH can be used to modify AH Plus sealer to eradicate residual bacteria and prevent reinfection.