Microstructure Characteristics of YBa₂Cu₃O₇- Nanocomposite by Shortening the Manufacturing Process

In this study, YBCO bulk was produced using two seeds by placing an additional seed on the upper pellet of the sample fabricated with the ISMG process. It was confirmed that the upper and lower pellets consisting of a-b sector showed a higher number of Y211 particles than those consisting of a-c sector, and that the same tendency appeared at a spot where different interfaces existed. This can be most clearly compared at the center. Finally, it was found that although minimizing the growth of a-c sector is an important goal for fabricating superconducting bulk magnets with high material properties, it is necessary to minimize the size of areas where different interfaces appear. It can be seen that the number of Y211 particles is the smallest inside the boundary surface, and that although they occupied a relatively smaller surface area, large particles agglomerated together.