Epitaxial GeSn Obtained by High Power Impulse Magnetron Sputtering and the Heterojunction with Embedded GeSn
Ioana Dascalescu1,2, Nicolae C Zoita3, Adrian Slav1
1National Institute of Materials Physics, 405A Atomistilor Street, 077125 Magurele, Romania.
Abstract:
GeSn alloys have the potential of extending the Si photonics functionality in shortwave infrared (SWIR) light emission and detection. Epitaxial GeSn layers were deposited on a relaxed Ge buffer on Si(100) wafer by using high power impulse magnetron sputtering (HiPI-MS). Detailed X-ray reciprocal space mapping and HRTEM investigations indicate higher crystalline quality of GeSn epitaxial layers deposited by Ge HiPI-MS compared to commonly used radio frequency magnetron sputtering (RF-MS). To obtain a rectifying heterostructure for SWIR light detection, a layer of GeSn nanocrystals (NCs) embedded in oxide was deposited on the epitaxial GeSn one. Embedded GeSn NCs are obtained by cosputtering deposition of (Ge1-Sn)1-(SiO2) layers and subsequent rapid thermal annealing at a low temperature of 400 °C. Intrinsic GeSn structural defects give p-type behavior, while the presence of oxygen leads to the n-character of the embedded GeSn NCs. Such an embedded NCs/epitaxial GeSn p-n heterostructure shows superior photoelectrical response up to 3 orders of magnitude increase in the 1.2-2.5 μm range, as compared to performances of diode based only on embedded NCs.