The effect of hydrogen bonding on diffusion and permeability in UV-cured Polyacrylate-based networks for controlled...

Polyacrylates are important polymers widely used in pharmaceutical industry such as drug coatings due to their low cost, processability and ease of functionalisation. Chemical functionalities (e.g. H-bonding) can be easily included to modulate the transport of low molecular weight drug-like entities through the network. Understanding how such microscopic structural modifications determine macroscopic diffusion is critical for designing next generation responsive polymers. In this study pulsed field gradient (PFG) ¹H NMR measurements of the self-diffusion of a dye molecule (Eosin Y) in a series of polyacrylate networks with differing H-bonding strength were undertaken; it was found that the diffusion of Eosin Y is significantly reduced in networks with H-bonding. Detailed analyses by ¹H NMR relaxometry and double quantum (DQ) NMR show that H-bonding can also reduce polymer chain mobility. Furthermore, DSC thermoporometry showed a significant increase in the average network mesh size potentially due to the pre-organization of H-bonding containing monomer during network curing. By introducing the H-bonding disrupter, LiClO₄, it was found that the diffusivity of solute becomes positively correlated to the average mesh size across the series of networks. Hence, a modified diffusion model based on hydrodynamic theory is proposed to separate the direct (solute-network) H-bonding contribution to solute diffusion from the indirect contribution arising from monomer pre-ordering induced mesh size reduction. Finally, it is shown that the same direct and indirect contributions to microscopic diffusivity, arising from the H-bond strength of the co-monomers, also contribute significantly to the macroscopic membrane permeability which is similarly subject to H-bond disruption.