Structural and magnetic properties of ultra-low density BiFeO₃ nanoparticles produced by pulsed laser deposition

Ultra-low-density BiFeO₃ nanoparticles have been prepared by pulsed laser deposition and their structure and magnetic properties have been studied. Annealing increases crystallinity and the size of the particles leading to an alteration of magnetic properties, observed from magnetic studies and evaluated using high-resolution transmission electron microscopy , selected area electron diffraction and x-ray diffraction patterns analysis. Transmission electron microscopy results show that the BiFeO₃ as-deposited nanoparticles annealed up to 400 °C exhibit a orthorhombic distorted perovskite structure without secondary phase and with diameters varying from 9 nm (as-deposited) to 17 nm (annealed at 400 °C). Magnetic data exhibit exchange bias and magnetic blocking effects at low temperatures and typical superparamagnetic behavior at high temperatures. Meanwhile, the BiFeO₃ nanoparticles annealed at 500 °C exhibit a rhombohedrally distorted perovskite structure with typical antiferromagnetic properties and diameter of about 56 nm. The analysis of magnetic relaxation time using the Arrhenius equation suggests a superparamagnetic blocking process of ferromagnetic clusters on the surface of the nanoparticles at low temperature. The magnetic properties are discussed considering the interactions between nanoparticles and the co-existence of different magnetic phases within the nanoparticles: an ordered antiferromagnetic core and ferromagnetic clusters on the surface.